Corrosion-induced cracking
Corrosion cracking - a type of quasi-brittle failure of steel and high-strength aluminum alloys under the simultaneous action of static tensile stresses and aggressive environments; characterized by the formation of single and multiple cracks associated with the concentration of main working and internal stresses. Cracks may propagate between crystals or through the grain body, but at a higher rate in the plane normal to the acting stresses than in the surface plane.
Source: "Guide for monitoring the condition of building metal structures of buildings and structures in aggressive environments, conducting surveys and designing restoration of protection of structures from corrosion (to SNiP 2.03.11-85)"
(approved by the order of TsIIIProektstal'konstruktsii dated 30.06.1987 No. 236)
Понятие «растрескивание коррозионное» среднего рода.
| Падеж | Единственное число | Множественное число |
|---|---|---|
| Р | растрескивания коррозионного | растрескивания коррозионного |
| Д | растрескиванию коррозионному | растрескиванию коррозионному |
| В | растрескивание коррозионное | растрескивание коррозионное |
| Т | растрескиванием коррозионным | растрескиванием коррозионным |
| П | растрескивании коррозионном | растрескивании коррозионном |